Effect of powder grinding on hydroxyapatite formation in a polymeric calcium phosphate cement prepared from tetracalcium phosphate and poly(methyl vinyl ether-maleic acid)

The primary aim of this study was to determine if cements based on poly(methyl vinyl ether-maleic acid) (PMVE-Ma) and tetracalcium phosphate resulted in hydroxyapatite formation. In addition, the mechanical strength of this type of polymeric calcium phosphate cement was evaluated. Cements were prepared by mixing, in a powder/liquid mass ratio of 3.0, an aqueous solution of PMVE-Ma (mass fraction=25%) and tetracalcium phosphate powders ground for various periods of time. The tetracalcium phosphate powders and set cements were characterized by means of X-ray powder diffraction and scanning electron microscopy. Mechanical strengths of the cements were tested 24 h after mixing. Prolonged grinding of tetracalcium phosphate powder decreased particle size and/or crystallite size and increased lattice distortion. This enhanced the reactivity of the tetracalcium phosphate powder and elevated the extent of crosslinking between PMVE-Ma molecules, resulting in improved mechanical strength. Hydroxyapatite formation was detected in the cement prepared with the most finely ground tetracalcium phosphate powder. The conversion of residual tetracalcium phosphate particles to more thermodynamically stable hydroxyapatite crystals will reduce the solubility of the polymeric cement and increase its biocompatibility.