Laser cutting: influence on morphological and physicochemical properties of polyhydroxybutyrate

Polyhydroxybutyrate (PHB) is a biocompatible and resorbable implant material. For these reasons, it has been used for the fabrication of temporary stents, bone plates, nails and screws (Peng et al. Biomaterials 1996;17:685). In some cases, the brittle mechanical properties of PHB homopolymer limit its application. A typical plasticizer, triethylcitrate (TEC), was used to overcome such limitations by making the material more pliable. In the past few years, CO2-laser cutting of PHB was used in the manufacturing of small medical devices such as stents. Embrittlement of plasticized PHB tubes has been observed, after laser machining. Consequently, the physicochemical and morphological properties of laser-processed surfaces and cut edges of plasticized polymer samples were examined to determine the extent of changes in polymer properties as a result of laser machining. These studies included determination of the depth of the laser-induced heat affected zone by polariscopy of thin polymer sections. Molecular weight changes and changes in the TEC content as a function of distance from the laser-cut edge were determined. In a preliminary test, the cellular response to the processed material was investigated by cell culture study of L929 mouse fibroblasts on laser-machined surfaces. The heat-affected zone was readily classified into four different regions with a total depth of about 60 to 100 μm (Klamp, Master Thesis, University of Rostock, 1998). These results correspond well with the chemical analysis and molecular weight measurements. Furthermore, it was found that cells grew preferentially on the laser-machined area. These findings have significant implications for the manufacture of medical implants from PHB by laser machining.