Ultrasensitive probing of the protein resistance of PEG surfaces by secondary ion mass spectrometry

The highly sensitive surface analytical techniques X-ray photoelectron spectroscopy (XPS) and time-of-flight static secondary ion mass spectrometry (ToF-SIMS) were used to test the resistance of poly(ethylene glycol) (PEG) coatings towards adsorption of lysozyme (LYS) and fibronectin (FN). PEG coatings were prepared by grafting methoxy-terminated aldehyde-PEG (MW 5000 Da) onto two amino-functionalised surfaces with different amine group densities, generated by radio frequency glow discharge polymerisation of n-heptylamine and allylamine. Grafting was performed at the lower critical solution temperature to maximise the graft density of the PEG chains. XPS showed that the grafted density of PEG chains was slightly higher on the allylamine surface. XPS detected no adsorption of either protein on either PEG coating. ToF-SIMS analysis, on the other hand, found, in the positive ion spectra, minute but statistically significant signals assignable to amino acid fragment ions from both proteins adsorbed to the lower density PEG coating and from LYS but not FN on the higher density PEG coating. Negative ion spectra contained relatively more intense protein fragment ion signals for the lower density PEG coating but no changes assignable to adsorbed proteins on the higher density PEG coating. These results demonstrate the importance of utilising highly sensitive techniques to study protein adsorption on surfaces intended to be protein resistant, and that both positive and negative ion ToF-SIMS spectra should be acquired to probe for possible very low levels of protein adsorption.