Exsolution and coarsening in iron-free clinopyroxene during isothermal annealing

Exsolution and coarsening in Fe-free clinopyroxene of composition En45.1Di54.9 was studied at temperatures of 1300, 1200, and 1100°C, and annealing times between 10 min and 4320 h. Based on the wavelength of the exsolution lamellae, the exsolution process can be divided into exsolution sensu stricto and coarsening. During exsolution sensu stricto, the average wavelength of the "001" and "100" lamellae remains constant in contrast to the subsequent coarsening process. A progressive development of the microstructure is observed before coarsening which includes formation of island-like regions of dark contrast without phase separation, occurrence of pigeonite and diopside domains predominantly elongated along (100), formation of "100" exsolution lamellae, dissolution of the "100" lamellae, and predominant occurrence of "001" exsolution lamellae. All observations are in accordance with the exsolution mechanism of spinodal decomposition. After termination of the exsolution process, coarsening of the exsolution lamellae is observed...