Preparation of alginate–chitosan hybrid gel beads and adsorption of divalent metal ions

Naturally occurring polysaccharides such as alginic acid and chitosan have been recognized as one of the most effective adsorbents to eliminating low levels of heavy metal ions from waste water stream. The present study intended to use alginic acid and chitosan simultaneously, which are expected to form a rigid matrix structure of beads due to electrostatic interaction between carboxyl groups on alginic acid and amino groups on chitosan, and to prepare alginate–chitosan hybrid gel beads. This could be achieved for the first time by using water-soluble chitosan, which was obtained by deacetylating chitin to 36–39% degree. The water-soluble chitosan dissolved in water could remain in solution in the presence of sodium alginate, and the homogeneous solution of chitosan and alginate was dispensed into a CuCl2 solution to give gel bead particles. The resultant beads were then reinforced by a cross-linking reaction of aldehyde groups on glutaraldehyde with amine groups on the chitosan. The cross-linking reaction made the beads durable under acidic conditions. The adsorption of Cu(II), Co(II), and Cd(II) on the beads was significantly rapid and reached at equilibrium within 10 min at 25 °C. Adsorption isotherms of the metal ions on the beads exhibited Freundlich and/or Langmuir behavior, contrary to gel beads either of alginate or chitosan showing a step-wise shape of adsorption isotherm.