Structural investigation of catalyst deactivation of Pt/SDB for catalytic oxidation of VOC-containing wastewater

The stability of styrene-divinyl benzene copolymer (SDB)-supported Pt (Pt/SDB) catalysts for destruction of volatile-organic-compound (VOC) in wastewater was examined. The test reaction was wet oxidation of water-containing aliphatic alcohol and formaldehyde at 140 °C and 90 psig for 40 h. The catalytic performance tests indicated that activity of the Pt/SDB catalysts could be maintained for VOC concentration of 3 wt.%, whereas the catalysts deactivated rapidly for 10 wt.% VOC containing wastewater. In order to investigate the nature of catalyst deactivation, extended X-ray absorption fine structure (EXAFS) and X-ray absorption near edge (XANES) spectroscopy were used to characterize the fresh and used catalysts. After the reaction, there is no oxidation of Pt clusters observed in EXAFS and XANES spectroscopy suggesting that the oxidation reaction takes places via the adsorbed oxygen. The spectroscopy results further indicated that deactivation of the catalysts were mainly caused by the increase of Pd particle size. After the reaction, the Pt–Pt coordination number has no significant change for the 3 wt.% wastewater whereas increase from 5.6 to 6.2 for 10 wt.% wastewater. Combined with the fact that the catalysts fractured during the reactions, we suggested that Pt agglomeration was mainly caused by thermal migration of the metal clusters.