The wetting behavior of NiAl and NiPtAl on polycrystalline alumina

In order to understand the beneficial effect of Pt on the adherence of thermally grown alumina scales, sessile drop experiments were performed to study the wetting of poly-crystalline alumina by nickel–aluminum alloys with or without platinum addition ranging from 2.4 to 10 at%. Subsequent interfacial morphology was examined using atomic force microscopy. Platinum addition enhances the wettability of NiAl alloys on alumina, reduces the oxide/alloy interface energy and increases the interfacial mass transport rates.