Sorption of cadmium(II) and zinc(II) ions from aqueous solutions by cassava waste biomass (Manihot sculenta Cranz)

The sorption of two divalent metal ions, Cd(II) and Zn(II), onto untreated and differentially acid-treated cassava waste biomass over a wide range of reaction conditions was studied at 30°C. The metal ion removal from the spent biomass was also measured. The batch experiments show that pH 4.5–5.5 was the best range for the sorption of the metal ions for untreated and acid-treated biomass. Time-dependent experiments for the metal ions showed that for the two metals examined, binding to the cassava waste biomass was rapid and occurred within 30 min and completed within 1 h. High sorption capacities were observed for the two metals. The binding capacity experiments revealed the following amounts of metal ions bound per gram of biomass: 86.68 mg/g Cd, 55.82 mg/g Zn and 647.48 mg/g Cd, 559.74 mg/g Zn for untreated and acid-treated biomass, respectively. It was further found that the rate of sorption was particle-diffusion controlled, and the sorption rate coefficients were determined to be 2.30×10^-1 min^-1 (Cd^2+), 4.0×10^-3 min^-1 (Zn^2+) and 1.09×10^-1 min^-1 (Cd^2+), 3.67×10^-2 min^-1 (Zn^2+) for 0.5 and 1.00 M differential acid treatment, respectively. Desorption studies showed that acid treatment inhibited effective recovery of metal ions already bound to the biomass as a result of stronger sulfhydryl-metal bonds formed. Less than 25% of both metals were desorbed as concentration of acid treating reagent increases. However, over 60% Cd and 40% Zn were recovered from untreated biomass during the desorption study. The results from these studies indicated that both untreated and acid-treated cassava waste biomass could be employed in the removal of toxic and valuable metals from industrial effluents.