Polyimide–silica hybrids containing novel phenylethynyl imide silanes as coupling agents for surface-treated titanium alloy

Polyimide–silica hybrids composed of an organic precursor containing a novel phenylethynyl imide silane and an inorganic precursor were evaluated as an adhesion-promoting interphase between surface-treated titanium alloy and a phenylethynyl-containing imide adhesive. The phenylethynyl groups present in the organic precursor, either as a pendent or end group, can bond chemically with a phenylethynyl-containing imide adhesive during processing, while the silane groups of the organic precursor would react chemically with the inorganic precursor. In addition, the inorganic precursor is able to react with the titanium alloy to form a stable bond with the metal oxide. Bond strength and durability were evaluated by single lap shear tests at various conditions. Lap shear specimens exhibited predominantly cohesive failure after a 3-d water boil with 92% retention of the initial room temperature strength. Morphology and chemical composition of the hybrid interphase were investigated with scanning electron microscopy, X-ray photoelectron spectroscopy, and Auger electron spectroscopy, which revealed development of a silicon-gradient, hybrid structure between the metal substrate and the adhesive.