Toughness investigation on simulated weld HAZs of SQV-2A pressure vessel steel Original Research Article

In order to get detailed information about weld HAZs toughness of SQV-2A steel and determine the optimum welding and heat treatment parameters, the toughness of simulated CGHAZs (coarse grained heat affected zone) and CGHAZs (intercritically reheated CGHAZ) were systematically investigated. The influence of tempering thermal cycles on weld ICCGHAZs toughness was clarified. The effect of post weld heat treatments (PWHT) on weld CGHAZs toughness was also determined. The results showed that high toughness (absorbed energy >200 J) of weld HAZs could be achieved by selecting the optimum welding and PWHT parameters (cooling time Δt8/5: 6–40 s, PWHT: 893 K, 3.6–7.2 ks). Tempering thermal cycles with peak temperature of above 573 K could remarkably improve the toughness of deteriorated ICCGHAZs and reduce the hardness, when cooling time Δt8/5(2) of the reheating thermal cycle was 6 s, which implies that welding of SQV-2A without PWHT is possible, provided that low heat input welding is adopted and welding procedure is correctly arranged. Metallography and fractography revealed that M–A constituents in weld HAZs played an important role in controlling weld HAZ toughness.