J-R fracture properties of SA508-1a ferritic steels and SA312-TP347 austenitic steels for pressurized water reactor’s (PWR) primary coolant piping Original Research Article

J-R fracture resistance of SA508-1a and SA312-TP347 steels, which are both rather peculiar as PWR primary coolant piping materials, were evaluated for application of leak-before-break methodology to the design basis of nuclear power plant piping. Archive materials from various heats of both steel pipes showed apparent heat-to-heat variations in ductile fracture resistance at the operating temperature 316°C. The SA508-1a ferritic steels showed relatively good J-R curve properties although they varied with the microstructures depending on the manufacturing process and chemical compositions. On the other hand, ductile crack growth resistance of SA312-TP347 austenitic stainless steel was unexpectedly poor when carbon content is moderately high. It was found that coarse niobium carbides deteriorated the ductile fracture resistance, so that more rigorous specification is needed in carbon and niobium contents to improve fracture properties of Type 347 stainless steels.