Effect of arabinose substitution on the material properties of arabinoxylan films Original Research Article

This study was undertaken to investigate the effect of arabinose content on film properties. The substrate used was a rye arabinoxylan that had an Ara/Xyl ratio of 0.52 and an average number molecular weight of 305 kDa. Oxalic acid was used to attempt selective removal of the arabinose substituents on the xylan main chain. The debranching of the polymer was coupled with a decrease in molecular weight. The effect of reaction conditions on the decrease in arabinose content and loss of molecular weight was investigated. Optimal conditions were selected using an experimental design. Treatment at lower temperature for longer period of times resulted in debranching with less degradation of the main chain. As the Ara/Xyl ratio was lowered, aggregates began to form in an interval of the Ara/Xyl ratio between 0.31 and 0.23 in a water solution. Precipitation occurred below an Ara/Xyl ratio of 0.1. Thus, removal of arabinose substituents results in a gradual association of unsubstituted chains. There is a linear correlation between arabinose substitution and the moisture content of arabinoxylan at 98% RH. A decrease in arabinose content resulted in the loss of a plasticizing effect, as determined by dynamic mechanical analysis, which is correlated to water binding capacity.