Structure and rheology of the κ-carrageenan/locust bean gum gels

The structure and interaction of κ-carrageenan and locust bean gum (LBG) has been studied using rheology, cryo-SEM, conductivity and syneresis characterization. The rheological behaviour of the binary system has been characterized using both compression and shear measurements. Elimination of slip in the shear measurements yields G′ values of the order 10,000–30,000 Pa for a 1% κ-carrageenan gel in 0–0.2 M added KCl. These values are higher than previously reported. No synergistic peak was found with the addition of LBG as has been previously reported. The measured modulii for these gels yields a Poissonʹs ratio of 0.5. Compression rupture stress and strain were also monitored. The rupture measurements do show a synergistic peak indicating that the interaction does occur and is important at high strain amplitudes. The gel points as determined by conductivity for these systems show a decrease in temperature with increasing LBG concentration, which is consistent with rheological measurements. Syneresis results are reported for the range of κ-carrageenan/LBG ratios. The syneresis shown by the mixtures is the same as that shown by the same concentration of κ-carrageenan. Structures of the gels as determined by cryo-SEM are also reported. Characteristic length scales in these systems are of the order of tens of microns and show little change with LBG concentration. The reduction in the characteristic length scale with increasing LBG concentration is discussed in terms of the rheological behaviour.