Atomic force microscopy of View the MathML source alloy formation on thin Au films

Atomic force microscopy was applied to the study of thin Au films deposited under ultra-high vacuum conditions on a glass support maintained at 78 K. A variety of thin gold film structures were thus determined and characterized ranging from (i) nanometric isolated gold islands, (ii) nanometric gold structures, to (iii) continuous gold films, all depending on the amount of Au deposited. The influence of the amalgamation process on the thin Au films topography was studied. The fundamental importance of surface defects on the rate of amalgamation was clearly seen. The movement of small Au islands on glass obtained as the result of thermal decomposition of View the MathML source alloys was observed.