Reducibility of ruthenium in relation with zeolite structure

Ru-zeolites prepared via deposition of aqueous solution of ruthenium chloride on X, L, ZSM-5 and APO-54 were investigated. The impregnated solids were characterized by the following techniques: N2sorption, H2chemisorption, TPR, XRD, XPS, EXAFS and Mo¨ssbauer spectroscopy. It was found that deposition of Ru is influenced by the pore structure and the chemical composition of the supports, in particular the concentration and strength of the protonic sites, with the formation of the different species. The packing of Ru as well as the degree of the reduction and the metal particle size are different according to the penetration depth of the metal and the nature of the zeolite. The amount of chlorine possibly remaining as adatoms of Ru is very low or inexistent. In calcined and reduced catalysts no chloride peak could be evidenced by XPS. The experiments confirmed that the use of large amounts of Ru chloride precursor leads to rather large metal particles. q1999 Elsevier Science B.V. All rights reserved.