Ethylene/Propylene Copolymerization Using Cp2ZrCI2/MAO Catalyst: Effects of Copolymerization Conditions on Viscosity Average Molecular Weight.

15

21

7

Copolymerization of ethylene with propylene is carried out semi-continuously in toluene at atmospheric pressure and with various propylene/ethylene molar ratios. The polymerization temperature and cocatalyst/catalyst molar ratio were also varied in a wide range. CP2ZrCI2/MAO System was used as catalyst. The viscosity average molecular weights of copolymers obtained were determined by measuring the intrinsic viscosity [TJ] and application of the Mark-Houwink equation. The values of molecular weights were found to be dependent on operating conditions except on polymerization time in the range 5-30 min. Increasing the polymerization temperature, propylene/ethylene and cocatalyst/catalyst molar ratios caused a continuous decrease in molecular weight. An important reason for this effect was shown to be accelerated chain transfer reactions.