On the flexural strength of self-healing E-glass/epoxy composites containing micro-vascular channels
پديدآورندگان :
Babolhavaeji M Faculty of Materials Science and Engineering, K. N. Toosi University of Technology, Tehran , Eslami-Farsani R eslami@kntu.ac.ir Faculty of Materials Science and Engineering, K. N. Toosi University of Technology, Tehran , Khosravi H Faculty of Materials Science and Engineering, K. N. Toosi University of Technology, Tehran
كليدواژه :
Self , healing , Micro , vascular channels , Flexural strength , Healing
عنوان كنفرانس :
پنجمين كنفرانس بين المللي كامپوزيت: مشخصه سازي، ساخت و كاربردها
چكيده فارسي :
Occurrence of damage is considered as an unavoidable fact in fiber-reinforced polymers (FRPs). For this
reason, the self-healing systems could extend the service life time of materials by implementing the concept of
autonomous or induced repair. In the present study, a self-healing E-glass/epoxy composite laminate based on microvascular
channels has been designed and fabricated. The self-healing system consists of vascular networks having two
various parts of ML-506 epoxy resin and HA-11 hardener. Micro-channels containing healing agent of 2 vol. % were
created in composites and the effect of healing time was considered. Here, the response of the specimens subjected to
three-point bending test was investigated. The highest recovery of flexural strength (about 65%) was observed after 7
days from the initial damage