عنوان مقاله :
Effect of Rolling Process on Mg/SiC Magnesium Matrix Composites
پديدآورندگان :
Mohammadi S School of Mechanical Engineering, Iran University of Science and Technology, Tehran, 16846-13114, Iran , Jabbari A. H a_jabbari@mecheng.iust.ac.ir School of Mechanical Engineering, Iran University of Science and Technology, Tehran, 16846-13114, Iran , Sedighi M School of Mechanical Engineering, Iran University of Science and Technology, Tehran, 16846-13114, Iran
كليدواژه :
Magnesium Matrix Composite , Mg , SiC , Powder Metallurgy , Rolling.
عنوان كنفرانس :
كنفرانس بين المللي دو سالانه مكانيك جامدات تجربي
چكيده فارسي :
In this paper, Mg composite containing SiC reinforcement particle has been fabricated using powder metallurgy (PM) process followed by hot rolling. First, 5 and 10 wt. % SiC powder (with average size of 15μm) has been added to Mg powder. Then they have been mixed by using high energy planetary ball-milling under argon atmosphere. In order to fabricate Mg/SiC composite, the mixture has been cold-compacted, sintered and finally hot-rolled in different temperatures and different number of passes. Microstructure and micro-hardness of the samples are investigated by optical microscopy and micro-Vickers hardness test, respectively. Microscopic evaluation of the hot-rolled composites shows a uniform distribution of SiC particles. No significant grain refinement is observed in the composite in comparison to monolithic Mg sample, while the hardness of samples has been increased by enhancing the number of rolling passes and SiC weight fraction.