The effect of plasticizer on ionic conductivity of the electrospun PEObased electrolytes applicable in lithium ion batteries
پديدآورندگان :
Banitaba Seyedeh Nooshin d_semnani@cc.iut.ac.ir Isfahan University of Technology , Semnani Dariush d_semnani@cc.iut.ac.ir Isfahan University of Technology , Rezaei Behzad d_semnani@cc.iut.ac.ir Isfahan University of Technology , Ensafi Ali Asghar d_semnani@cc.iut.ac.ir Isfahan University of Technology
كليدواژه :
Li ion battery , Electrospun electrolyte , Ion conductivity , Propylene carbonate , Plasticizer.
عنوان كنفرانس :
چهاردهمين سمينار ملي سالانه الكتروشيمي ايران
چكيده فارسي :
Herein, fabrication of all-solid-state PEO-LiClO4 nanofibrous electrolytes by using an electrospinning process was reported. The effect of propylene carbonate (PC) on morphology and electrochemical properties of the electrospun electrolytes was evaluated. The results showed that the average diameter of the nanofibers was decreased with the addition of PC. In addition, flatshaped nanofibers were obtained in the absence of PC. Ion conductivity of 0.05 mS.cm-1 was approached with the addition of PC into the nanofibrous electrolytes. Moreover the as-spun electrolyte showed good cycling stability after 20 cycles.