عنوان مقاله :
Conductivity study of the electrospun PEO-based electrolytes incorporated with TiO2 nanoparticles for use in Lithium ion batteries
پديدآورندگان :
Banitaba Seyedeh Nooshin n.banitaba@tx.iut.ac.ir Isfahan University of Technology , Semnani Dariush n.banitaba@tx.iut.ac.ir Isfahan University of Technology , Rezaei Behzad n.banitaba@tx.iut.ac.ir Isfahan University of Technology , Ensafi Ali Asghar n.banitaba@tx.iut.ac.ir Isfahan University of Technology
كليدواژه :
Li ion battery , Electrospun electrolyte , Ion conductivity , TiO2 nanoparticle.
عنوان كنفرانس :
چهاردهمين سمينار ملي سالانه الكتروشيمي ايران
چكيده فارسي :
In this study, all-solid-state PEO-based nanofibrous electrolytes were fabricated by an electrospinning method. LiClO4 and ethylene carbonate (EC) were applied as lithium salt and plasticizer, respectively. The effect of TiO2 nanoparticles were studied on the morphology and ion conductivity of the as-spun electrolytes. The results showed reduction of average diameter of the nanofibers with introduction of TiO2 to electrospun electrolytes. In addition, ion conductivity of about 0.08 mS.cm-1 was obtained with the addition of 3 wt. % TiO2 to the electrospun nanofibers.