عنوان مقاله :
Characterization and Corrosion Resistance of Electrodeposited Ni–Mo–Coating on Stainless Steel Substrates with an Alkaline Electrolytic Bath
پديدآورندگان :
bagherabadi Mohammadhassan Department of Chemistry, Isfahan University of Technology, Isfahan, 84156-83111, Islamic Republic of Iran , zhiani mohammad Department of Chemistry, Isfahan University of Technology, Isfahan, 84156-83111, Islamic Republic of Iran
كليدواژه :
electrodeposition , nicke , molybdenum , stainless steel , three , electrode cell
عنوان كنفرانس :
بيست و يكمين كنفرانس ملي شيمي فيزيك انجمن شيمي ايران
چكيده فارسي :
A study on the electrocatalytic performances of nickel–molybdenum that were prepared by electrodeposition. During the electrocodeposition process of Ni–Mo coating on stainless steel substrates with an alkaline electrolytic bath containing of different material such as NiSO4·6H2O, Na2MoO4·2H2O, H3BO3 and Na3C6H5O7·2H2O [1,2,3]. After preparing, electrodeposition process was performed in a three-electrode cell in which saturated calomel electrode was used as a reference electrode, Pt gauze as counter electrode and stainless steel as working electrode. The plating solution was purged with N2 for 10 min before deposition. Pulsed electrodeposition was used to prepare Ni–Mo using a potential of −1.303V for 10 s then −0.862V for 3 s until a total charge of 100 C was reached [4,5].