Epoxy’s toughening by CO2 fixation reaction
پديدآورندگان :
Ghanbaralizadeh R نويسنده , Bouhendi Hosein نويسنده , Amiri F نويسنده Physics Department, College of Sciences, Shiraz University, Shiraz, Iran , Kabiri Keivan نويسنده Iranian National Institute for Oceanography , Vafaeean M نويسنده
كليدواژه :
CO2 fixation , Toughness , mechanical properties , Epoxy
عنوان كنفرانس :
The 6 th International Color & Coating Congress
چكيده فارسي :
Bifunctional epoxy resin (DGEBPA) was modified by CO2 fixation reaction in the presence of Tetra-n-butyl ammonium bromide (TBAB) as catalyst. Cycloaliphatic component as a reactive diluent was used in order to viscosity reduction, UnModified Epoxy resin (UME) and CO2 Fixed Epoxy resin (CFME) at different amount of carbonation were cured by diethylen three amine (DETA) as curing agent, and effect of carbonation on mechanical properties was investigated. Flexural properties were investigated by 3.point bending test. Fracture toughness test showed the toughness of epoxy resin in terms of the critical-stress-intensity factor, KIC raised from 0.7 to 1.58(MPa.m1/2). A smooth and flat fracture surface morphology for UME and a rough fracture surface morphology for CFME were characterized by scanning electron microscopy (SEM).
شماره مدرك كنفرانس :
4184098