TEKER, Dilek İstanbul Technical University - Department of Metallurgical and Materials Engineering, Turkey , MUHAFFEL, Faiz Ýstanbul Technical University - Department of Metallurgical and Materials Engineering, Turkey , ÇİMENOĞLU, Hüseyin İstanbul Technical University - Department of Metallurgical and Materials Engineering, Turkey

Characterization and In Vitro Bioactivity of Calcium and Phosphorous Containing Titania Layer on Ti6Al4V Alloy

25401

Calcium and phosphorous containing titania layers on Ti6Al4V biomedical alloy were formed by micro arc oxidation (MAO) in an electrolyte containing calcium acetate and sodium phosphate, and then subjected to hydrothermal treatment (HT) in order to achieve improved biocompability with modified titania layer. Samples were hydrothermally treated in water solution whose pH was adjusted to 11.0-11.5 by adding NaOH, at 230 °C for 10 h and cooled in the autoclave. Surface morphology, microstructure, and phase composition of titania layer were investigated systematically before and after HT. Their biomimetic apatite inducing ability in a simulated body fluid (SBF) was investigated. The bioactivity tests of modified MAO surface on Ti6Al4V alloy showed a considerable improvement compared to the unmodified MAO surface.

147

Ti6Al4V. Micro Arc Oxidation. Titania layer. Hydrothermal Treatment. Bioactivity.

Journal Of Natural an‎d Applied Sciences

151