AKDOĞAN, Erkin Pamukkale Üniversitesi - Mühendislik Fakültesi - Makine Mühendisliği Bölümü, Türkiye , TARAKCILAR, Ali Rıza Pamukkale Üniversitesi - Mühendislik Fakültesi - Makine Mühendisliği Bölümü, Turkey , TOPÇU, Muzaffer Pamukkale Üniversitesi - Mühendislik Fakültesi - Makine Mühendisliği Bölümü, Turkey , YURTSEVEN, Recep

THE EFFECTS OF ALUMINIUM HYDROXIDE AND MAGNESIUM HYDROXIDE ON THE MECHANICAL PROPERTIES OF THERMOPLASTIC POLYURETHANE MATERIALS

40776

Thermoplastic polyurethane materials are widely used in automotive, clothing, electrical and electronics, medical, construction, machine industry due to excellent physical and chemical properties. Thermoplastic polyurethane materials combustion and resistance to high temperature characteristics are poor. Additives and fillers are added into the polyurethane matrix to improve those properties. Particularly adding these agents as a flame retardant are affect mechanical properties of polyurethane materials. Therefore, it is important to determinate the mechanical properties of these materials. In this study, 5% by weight of the thermoplastic polyurethane material, aluminium tri hydroxide (ATH, (Al2O3 3H2O)) and magnesium hydroxide (MgOH, (Mg(OH)2)) were added. Ammonium polyphosphate (APP) as an intumescent flame retardant with inorganic flame retardants were added to increase the flame resistance of produced composite structure. Tensile test, tear test, hardness and Izod impact tests were made and compared of those produced composites. As a result of experiments the addition of ATH has lowered the tensile strength and tear strength contrast to this the addition of MgOH has improved those properties. Hardness and Izod impact test results were showed that both of the additives have no negative effect.

376

Thermoplastic polyurethane , Aluminium tri hydroxide , Magnesium hydroxide , Tensile strength , Tear strength

Pamukkale University Journal Of Engineering Sciences

380