The properties of CoCrPt/CrMn/NiAl and CoCrPt/Cr/NiAl films

Author

Zou, Jie ; Lu, Bin ; Laughlin, David E. ; Lambeth, David N.

Author_Institution

Data Storage Syst. Center, Carnegie Mellon Univ., Pittsburgh, PA, USA

Volume

35

Issue

5

fYear

1999

fDate

9/1/1999 12:00:00 AM

Firstpage

2661

Lastpage

2663

Abstract

In this study, the effects of CrMn/NiAl and Cr/NiAl underlayers on microstructure and magnetic properties of CoCrPt magnetic layers are compared. CrMn intermediate layers were found to induce better in-plane texture and magnetic properties in CoCrPt films than Cr. Significant improvement in magnetic properties was achieved by post-deposition rapid thermal annealing (RTA). The anisotropy did not decrease much while grain isolation in the CoCrPt layer was achieved by using RTA

Keywords

chromium alloys; cobalt alloys; grain size; magnetic anisotropy; magnetic thin films; platinum alloys; rapid thermal annealing; texture; CoCrPt magnetic film; CoCrPt-Cr-NiAl; CoCrPt-CrMn-NiAl; Cr/NiAl underlayer; CrMn/NiAl underlayer; anisotropy; grain isolation; intermediate layer; magnetic properties; microstructure; rapid thermal annealing; texture; Anisotropic magnetoresistance; Chromium; Coercive force; Grain boundaries; Magnetic anisotropy; Magnetic films; Magnetic materials; Magnetic properties; Microstructure; Perpendicular magnetic anisotropy;

fLanguage

English

Journal_Title

Magnetics, IEEE Transactions on

Publisher

ieee

ISSN

0018-9464

Type

jour

DOI

10.1109/20.800938

Filename

800938