Phase transitions and dielectric properties in Bi(Zn1/2Ti1/2)O3-ABO3 perovskite solid solutions

Author

Huang, Chien-Chih ; Cann, David P.

Author_Institution

Department of Mechanical Engineering, Oregon State University, Corvallis, 97331-6001, USA

Volume

1

fYear

2008

Firstpage

1

Lastpage

3

Abstract

A group of (1??x)Bi(Zn1/2Ti1/2)O3-??ABO3 (ABO3=BaTiO3, NaNbO3, BiScO3 and Bi1/2K1/2TiO3) polycrystalline ceramics were prepared by solid-state processing techniques. Based on x-ray diffraction results, the presence of Bi(Zn1/2Ti1/2)O3 in the solid solution decreases the structure stability of perovskite phase. The dielectric characterization revealed that the trends of transition temperature Tm as a function of composition of Bi(Zn1/2Ti1/2)O3-ABO3 could be described into two groups. The first one is Tm decreased until second phase appeared and the second one is Tm decreased and then increased as Bi(Zn1/2Ti1/2)O3 content increased. In addition, with substitution of Li for Na of NaNbO3-Bi(Zn1/2Ti1/2)O3 the diffuseness of the transition peak decreased and transition temperature increased.

Keywords

Bismuth; Ceramics; Dielectrics; Ferroelectric materials; Piezoelectric materials; Powders; Solid state circuits; Stability; Temperature; X-ray diffraction; Ferroelectric; Pervoskites; Piezoelectricity;

fLanguage

English

Publisher

ieee

Conference_Titel

Applications of Ferroelectrics, 2008. ISAF 2008. 17th IEEE International Symposium on the

Conference_Location

Santa Re, NM, USA

ISSN

1099-4734

Print_ISBN

978-1-4244-2744-4

Electronic_ISBN

1099-4734

Type

conf

DOI

10.1109/ISAF.2008.4693889

Filename

4693889