The growth of aligned Cu/sub 2/S nanowire arrays with AAO template by gas-solid reaction
Author
Wu, Q.B. ; Ren, S. ; Deng, S.Z. ; Jun Chen ; Xu, N.S.
Author_Institution
State Key Lab. of Optoelectron. Mater. & Technol., Zhongshan Univ., Guangzhou, China
fYear
2003
fDate
7-11 July 2003
Firstpage
197
Lastpage
198
Abstract
The details are given of an experimental study of the growth process of aligned Cu/sub 2/S nanowire arrays with anodic aluminum oxide (AAO) template by a gas-solid reaction. It was found that the template played an important role in the control growth with good alignment. The nanowire arrays had similar diameter (about 100 nm) and height (about 1 /spl mu/ m). Their electron field emission property was also measured. A turn-on field of 2.2 MV/m and a threshold-field of 8 MV/m were observed, respectively.
Keywords
aluminium compounds; copper compounds; field emitter arrays; nanotechnology; nanowires; sputter deposition; 1 micron; 100 nm; Cu/sub 2/S-Al/sub 2/O/sub 3/; aligned Cu/sub 2/S nanowire arrays growth; anodic aluminum oxide template; electron field emission; gas-solid reaction; Aluminum; Cathodes; Copper; Electron emission; Laboratories; Nanoporous materials; Nanoscale devices; Scanning electron microscopy; Sun; Surface morphology;
fLanguage
English
Publisher
ieee
Conference_Titel
Vacuum Microelectronics Conference, 2003. Technical Digest of the 16th International
Conference_Location
Osaka, Japan
Print_ISBN
4-8181-9515-4
Type
conf
DOI
10.1109/IVMC.2003.1223051
Filename
1223051
Link To Document