Evaluation of plasma-sprayed CoS2 cathodes for thermal batteries

Conventional electroactive stack components in thermal batteries are constructed from pressed-powder parts. These include the anode, separator, and cathode pellets (discs). Pressing parts that are less than 0.010" thick is difficult. The use of plasma spray to deposit thin CoS/sub 2/ cathode films onto a stainless steel substrate was examined as an alternative to pressed-powder cathodes. The plasma-sprayed electrodes were tested in single cells under isothermal conditions and constant-current discharge over a temperature range of 400/spl deg/C to 550/spl deg/C using standard LiSi anodes and separators based on the LiCl-KCl eutectic. Similar tests were conducted with cells built with conventional pressed-powder cathodes, which were tested under the same conditions for comparative purposes. This paper presents the results of those tests.