An investigation on the applicability of eddy currents NDT to the inspection of corrosion-fatigue phenomena in railway axles
Author :
Carboni, M. ; Beretta, S. ; Lo Conte, A.
Author_Institution :
Dept. Mech. Eng., Politec. di Milano, Milan, Italy
Abstract :
Recent experience with existing railway axles indicates that even when they are operated within the design loads, failure can happen due to the synergetic effect of both corrosion and cyclic loads. This synergy is not yet thoroughly understood, however a need for detecting corrosion-fatigue during service is mandatory. The present paper describes the investigations, carried out during a recent international scientific cooperation (RSSB T728) and an ongoing European Project (WOLAXIM), on the possibility to apply eddy currents non destructive inspection to the detection of corrosion pits and corrosion-fatigue cracks during the service of railway axles.
Keywords :
axles; corrosion fatigue; corrosion testing; eddy current testing; failure (mechanical); fatigue cracks; inspection; railways; European Project; RSSB T728; WOLAXIM; corrosion fatigue phenomena; corrosion load; corrosion pit detection; corrosion-fatigue crack detection; cyclic load; design loads; eddy current NDT; eddy current nondestructive inspection; eddy current nondestructive testing; failure; international scientific cooperation; railway axle service; synergetic effect; RSSB T728; WOLAXIM; corrosion-fatigue; eddy currents inspection; railway axles;
Conference_Titel :
Railway Condition Monitoring and Non-Destructive Testing (RCM 2011), 5th IET Conference on
Conference_Location :
Derby
DOI :
10.1049/cp.2011.0601