Title :
Influence of annealing method on the space charge properties in polyethylene
Author :
Wang, Ninghua ; Zhou, Yuanxiang ; Hongbin Liu ; Gao, Bin ; Liang, Xidong ; Guan, Zhicheng ; Takada, Tatsuo
Author_Institution :
Dept. of Electr. Eng., Tsinghua Univ., Beijing, China
Abstract :
In this paper, high-density polyethylene (HDPE) films were prepared by three kinds of annealing methods which were different in cooling speed. The crystallinity of those HDPE samples were measured and compared. A high DC voltage was applied to the samples and the space charge formed was measured. Homo-charges were found in samples that were applied with a negative high voltage. The space charge properties were discussed, based on crystallinity. From these results, it is found that the space charge formed in samples cooled at high speed is more than that of the samples cooled at normal and low speed.
Keywords :
annealing; charge measurement; crystal microstructure; crystal morphology; crystallisation; polyethylene insulation; polymer films; space charge; HDPE film crystallinity; annealing; cooling speed; high-density polyethylene films; homocharges; morphological microstructure; polyethylene morphology; polyethylene space charge properties; space charge formation; space charge measurement; Annealing; Charge measurement; Conducting materials; Crystallization; Current measurement; Laboratories; Morphology; Polyethylene; Space charge; Voltage;
Conference_Titel :
Electrical Insulation and Dielectric Phenomena, 2004. CEIDP '04. 2004 Annual Report Conference on
Print_ISBN :
0-7803-8584-5
DOI :
10.1109/CEIDP.2004.1364190