Title :
Pattern of brittle layer cracking under tension of coated specimens
Author :
Koval, Anna ; Panin, Sergey
Author_Institution :
Tomsk Polytech. Univ., Russia
fDate :
26 Jun-3 Jul 2001
Abstract :
In the given work peculiarities of plastic deformation and fracture of compositions with gradient coatings under static uniaxial tension were investigated. Surface hardening was performed by diffusion borating. The studying of cracking processes of. borated layers was carried out by analysis of the plane face of working parts of failured specimens with the use of the TESLA BS 300 scanning electron microscope
Keywords :
brittle fracture; cracks; plastic deformation; scanning electron microscopy; surface hardening; SEM; borated layers; brittle layer cracking pattern; coated specimens tension; diffusion borating; gradient coatings; plastic deformation; scanning electron microscopy; static uniaxial tension; surface hardening; Coatings; Equations; Gaussian processes; Needles; Physics; Plastics; Scanning electron microscopy; Steel; Surface cracks; Testing;
Conference_Titel :
Science and Technology, 2001. KORUS '01. Proceedings. The Fifth Russian-Korean International Symposium on
Conference_Location :
Tomsk
Print_ISBN :
0-7803-7008-2
DOI :
10.1109/KORUS.2001.975116