Research on heat-resistance and corrosion of glass flake/boron modified silicone coating
Author
Zhang, Aili ; Liu, Hai ; Wu, Songhao
Author_Institution
School of Environmental and Chemical Engineering, Shen Yang Ligong University, Shen Yang, China
fYear
2011
fDate
9-11 Sept. 2011
Firstpage
3888
Lastpage
3891
Abstract
A kind of high heat-resistance and corrosion coating which can be used to resist at 550°C, salt spray resistance time to 168h was prepared by boron modified silicone resin for raw material, glass flake as filler, titanium dioxide as pigment, silane coupling agent as additives. The results showed that the optimal coating performance was obtained at pigment grinding time 2h, high speed dispersion coatings 2h, the pigment to binder ratio of 0.3:1, KH-560 account for the total coatings 2.1%, glass flake pigments account for the mass ratio of 75%. The paint film has good Conventional performance.
Keywords
Boron; Coatings; Corrosion; Glass; Pigments; Resins; Resistance; anti-corrosion coating; boron modified silicone resin; glass flake; high temperature;
fLanguage
English
Publisher
ieee
Conference_Titel
Electronics, Communications and Control (ICECC), 2011 International Conference on
Conference_Location
Ningbo, China
Print_ISBN
978-1-4577-0320-1
Type
conf
DOI
10.1109/ICECC.2011.6067986
Filename
6067986
Link To Document