Failure Analysis and Improved Method of Batch Cracks for Certain Fighter Aircraft
Author
Wei Zhang ; Desheng Yu ; Dongdong Qi ; Hongling Qi ; Dan Xu
Author_Institution
East China Jiaotong Univ., Nanchang, China
fYear
2014
fDate
19-21 Dec. 2014
Firstpage
150
Lastpage
154
Abstract
52 cracks of different length appeared around R corner of counterweight angles were checked in 30 service fighter aircrafts, which affected the completion of the flight training seriously. Based on the parts inspection, strength check and stress of broken components, combined with the results of failure fracture about physicochemical analysis, analyzed cracks on the aileron angle. This paper concluded that the main cause of cracks which is the fatigue source cause of the structure details of the design defects and details of manufacturing defects, and proposed the strengthening scheme about this kind of cracks.
Keywords
aircraft; cracks; failure (mechanical); fracture; batch cracks; counterweight angles; failure analysis; failure fracture; fighter aircraft; flight training; physicochemical analysis; strength check; Aircraft; Connectors; Fatigue; Finite element analysis; Manufacturing; Stress; Surface cracks;
fLanguage
English
Publisher
ieee
Conference_Titel
Computational Science and Engineering (CSE), 2014 IEEE 17th International Conference on
Conference_Location
Chengdu
Print_ISBN
978-1-4799-7980-6
Type
conf
DOI
10.1109/CSE.2014.59
Filename
7023570
Link To Document