Enhancement of breakdown strength of polyetherimide laminates

Author

Zheng, J.P. ; Cygan, P.J. ; Jow, T.R.

Author_Institution

Army Res. Lab., Fort Monmouth, NJ, USA

fYear

1993

fDate

17-20 Oct 1993

Firstpage

390

Lastpage

395

Abstract

The breakdown strength of polymer laminates, polymer base films coated with thin layers of polyvinylidene fluoride (PVDF), was investigated. The PVDF film was coated using a spin coating technique. The DC breakdown strength was studied using an ASTM standard and could be increased by as much as 20% for the polyetherimide laminates. It was found that this breakdown strength was insensitive to the thickness of the polymer base films and the PVDF films. Other dielectric properties such as the dielectric constant dissipation factor were also studied for the samples with and without PVDF coatings. Possible mechanisms for the enhancement of breakdown strength are discussed

Keywords

composite insulating materials; electric breakdown; electric strength; laminates; organic insulating materials; permittivity; polymer films; ASTM standard; DC breakdown strength; PVDF film; breakdown strength; dielectric constant dissipation factor; polyetherimide laminates; polymer base films; polymer laminates; polyvinylidene fluoride; spin coating technique; Capacitors; Coatings; Dielectric materials; Electric breakdown; Electrodes; Laminates; Polymer films; Rough surfaces; Surface morphology; Surface roughness;

fLanguage

English

Publisher

ieee

Conference_Titel

Electrical Insulation and Dielectric Phenomena, 1993. Annual Report., Conference on

Conference_Location

Pocono Manor, PA

Print_ISBN

0-7803-0966-9

Type

conf

DOI

10.1109/CEIDP.1993.378941

Filename

378941