A dangerous type of failure mode of aircraft PTFE hose assembly and reliability measures
Author
Wang, Xinkun ; Xi, Shenghai ; Chen, Yi
Author_Institution
Beijing Aeronaut. Technol. Res. Center, Beijing, China
fYear
2012
fDate
15-18 June 2012
Firstpage
1309
Lastpage
1313
Abstract
By means of macro and micro aspect examination, the two different mechanisms which lead to the high pressure PTFE hose crack has been studied. The results show that the wrong installation and the nick on the inner surface of the PTFE hose are the primary factors which influence the reliability of the PTFE hose during in commission. In the course of using, micro-cracks gradually develop into cracks and lead to the hose beginning to leak. Improving reliabilities measures have been discussed from the installation.
Keywords
aerospace components; aerospace materials; ageing; aircraft maintenance; crack detection; fatigue cracks; hoses; polymers; reliability; aircraft PTFE hose assembly; failure mode; macroaspect examination; microaspect examination; microcracks; reliability measure; Assembly; Hoses; Liquids; Maintenance engineering; Reliability; Servomotors; Surface cracks; PTFE hose assembly; crack; failure mode; nick; reliability measure;
fLanguage
English
Publisher
ieee
Conference_Titel
Quality, Reliability, Risk, Maintenance, and Safety Engineering (ICQR2MSE), 2012 International Conference on
Conference_Location
Chengdu
Print_ISBN
978-1-4673-0786-4
Type
conf
DOI
10.1109/ICQR2MSE.2012.6246462
Filename
6246462
Link To Document