Nano-silver paste with low roasting temperature

Author

Wang, Xiuyu ; Zhang, Zhisheng

Author_Institution

Sch. of Electron. Inf. Eng., Tianjin Univ., China

fYear

2005

fDate

30 Aug.-2 Sept. 2005

Firstpage

226

Lastpage

228

Abstract

A kind of new silver paste with silver content about 50wt%, nano-silver paste, significantly different with normal silver paste in roasting temperature, was prepared using nano-silver powder, ethanol, n-butyl alcohol, n-hexyl alcohol and low polymer fibre. The nano-silver paste shows weight loss and volatilization with different levels on thermogravimetric (TG) analyzing curve. Field emission scanning electron microscope (FESEM) analysis indicates when roasting temperature is controlled at 200°C, the surface of finished silver film has already been compact and smooth. And finished silver film has stronger adhesive with ceramic and mental substrates, while the adhesive is poor with slippery glass. The minimal square resistor of obtained silver film can reach 7.8mΩ/□.

Keywords

field emission electron microscopes; nanoparticles; scanning electron microscopes; silver; surface finishing; thermal analysis; thin films; 200 C; Ag; ceramic substrates; ethanol; field emission scanning electron microscope analysis; finished silver film; low polymer fibre; low roasting temperature; minimal square resistor; n-butyl alcohol; n-hexyl alcohol; nano-silver paste; nano-silver powder; thermogravimetric analyzing curve; Ceramics; Electron emission; Ethanol; Polymers; Powders; Scanning electron microscopy; Silver; Substrates; Surface finishing; Temperature control;

fLanguage

English

Publisher

ieee

Conference_Titel

Electronic Packaging Technology, 2005 6th International Conference on

Print_ISBN

0-7803-9449-6

Type

conf

DOI

10.1109/ICEPT.2005.1564619

Filename

1564619