The current annealing in Co-based glass-covered amorphous microwires

Author

Tian Bin

Author_Institution

Sch. of Electr. & Inf. Eng., Wuhan Inst. of Technol., Wuhan, China

fYear

2011

fDate

15-17 April 2011

Firstpage

808

Lastpage

809

Abstract

The effect of current annealing on magnetic properties and giant magneto-impedance effect of Co-rich glass-covered microwires have been studied. The magnetic properties of four samples that are as cast, Joule-heated under dc current or ac current of 100 Hz or 500 Hz is compared. It was concluded that longitudinal anisotropy dominates the microwire behaviour. But, the inner core with longitudinal anisotropy is surrounded by two concentric outer shells with almost circumferential anisotropies by current annealing. Furthermore,the GMI ratio of the sample under dc current annealing is higher than the GMI ratio of the samples under ac current annealing for the stable magnetic field that induces stronger circumferential anisotropy is produced by dc current annealing.

Keywords

amorphous magnetic materials; cobalt; giant magnetoresistance; magnetic annealing; Co; concentric outer shells; current annealing; giant magneto-impedance effect; glass-covered amorphous microwires; longitudinal anisotropy; magnetic properties; Amorphous magnetic materials; Annealing; Magnetic domains; Magnetic fields; Perpendicular magnetic anisotropy; Wires; Giant magneto-impedance; Glass-covered microwires; Joule heating;

fLanguage

English

Publisher

ieee

Conference_Titel

Electric Information and Control Engineering (ICEICE), 2011 International Conference on

Conference_Location

Wuhan

Print_ISBN

978-1-4244-8036-4

Type

conf

DOI

10.1109/ICEICE.2011.5778033

Filename

5778033