A Two-Step-Recess Process Based on Atomic-Layer Etching for High-Performance $\hbox {In}_{0.52}\hbox {Al}_{0.48}\hbox {As}\hbox {/}\hbox {In}_{0.53} \hbox {Ga}_{0.47}\hbox {As}$

We investigated 60-nm In_0.52Al_0.48As/In_0.53Ga_0.47As pseudomorphic high-electron mobility transistors (p-HEMTs) fabricated by using a Ne-based atomic-layer-etching (ALET) technology. The ALET process produced a reproducible etch rate of 1.47 Aring/cycle for an InP etch stop layer, an excellent InP etch selectivity of 70 against an In_0.52Al_0.48As barrier layer, and an rms surface-roughness value of 1.37 Aring for the exposed In_0.52Al_0.48As barrier after removing the InP etch stop layer. The application of the ALET technology for the gate recess of 60-nm In_0.52Al_0.48As/In_0.53Ga_0.47As p-HEMTs produced improved device parameters, including transconductance (G_M), cutoff frequencies (f_T)> and electron saturation velocity (vsat) in the channel layer, which is mainly due to the high etch selectivity and low plasma-induced damage to the gate area. The 60-nm In_0.52Al_0.48As/In_0.53Ga_0.47As p-HEMTs fabricated by using the ALET technology exhibited G_M,_Max = 1-17 S/mm, f_T = 398 GHz, and v_sat = 2.5 X 10⁷ cm/s.