Improved Ge Surface Passivation With Ultrathin SiOX Enabling High-Mobility Surface Channel pMOSFETs Featuring a HfSiO/WN Gate Stack

To realize high-mobility surface channel pMOSFETs on Ge, a 1.6-nm-thick SiO_X passivation layer between the bulk Ge substrate and HfSiO gate dielectric was introduced. This approach provides a simple alternative to epitaxial Si deposition followed by selective oxidation and leads to one of the highest peak hole mobilities reported for unstrained surface channel pMOSFETs on Ge: 332 cm² middotV^-1middots^-1 at 0.05 MV/cm-a 2times enhancement over the universal Si/SiO₂ mobility. The devices show well-behaved output and transfer characteristics, an equivalent oxide thickness of 1.85 nm and an I_ON/I_OFF ratio of 3times10³ without detectable fast transient charging. The high hole mobility of these devices is attributed to adequate passivation of the Ge surface