The Effect of Recovery Annealing on the Magnetic and Mechanical Properties of Nonoriented Electrical Steels

Author

Rodrigues Junior, Daniel Luiz ; Nishikawa, Thomas S. P. ; Almeida, Adriano A. ; Landgraf, Fernando J. G. ; Martin, Ramon V.

Author_Institution

Dept. of Eng. Metalurgica e de Mater., Univ. de Sao Paulo, São Paulo, Brazil

Volume

50

Issue

4

fYear

2014

fDate

Apr-14

Firstpage

1

Lastpage

4

Abstract

Recovery annealing was studied in Fe-0.7Si electrical steel processed by cold rolling. The samples were annealed at temperatures of 300°C, 400°C, and 500°C for 30, 60, and 90 min in inert nitrogen atmosphere. No samples suffered recrystallization. From these samples, magnetic losses and the value of yield strength by means of tensile test were obtained. From these data the higher sensitivity to the recovery of the magnetic properties characterized by the magnetic losses when compared with the mechanical properties represented by the yield strength could be seen.

Keywords

annealing; cold rolling; eddy current losses; steel; tensile testing; yield strength; cold rolling; electrical steels; magnetic losses; magnetic properties; mechanical properties; nitrogen atmosphere; recovery annealing effect; recrystallization; temperature 300 degC to 500 degC; tensile test; time 30 min to 90 min; yield strength; Annealing; Loss measurement; Magnetic hysteresis; Magnetic properties; Magnetomechanical effects; Steel; Strain; Electrical steel; excess loss; magnetic properties; recovery annealing;