Role of positive trapped charge in stress-induced leakage current for flash EEPROM devices

The transient behavior of hot hole (HH) stress-induced leakage current (SILC) in tunnel oxides is investigated. The dominant SILC mechanism is positive oxide charge-assisted tunneling (PCAT). The transient effect of SILC is attributed to positive oxide charge detrapping and thus the reduction of PCAT current. A correlation between SILC and stress-induced substrate current is observed. Our study shows that both SILC and stress-induced substrate current have power law time-dependence t^-n with the power factor n about 0.7 and 1, respectively. Numerical analysis for PCAT current incorporating a trapped charge caused Coulombic potential in the tunneling barrier is performed to evaluate the time- and field-dependence of SILC and the substrate current. Based on our model, the evolution of threshold voltage shift with read-disturb time in a flash EEPROM cell is derived. Finally, the dependence of SILC on oxide thickness is explored. As oxide thickness reduces from 100 Å to 53 Å, the dominant SILC mechanism is found to change from PCAT to neutral trap-assisted tunneling (TAT).