Title :
Effects of P addition on magnetic interactions and microstructures in Co-Cr-P-Pt magnetic thin films
Author :
Sohn, H.K. ; Shin, K.H. ; Lee, T.D. ; Kang, T. ; Sung, C.M.
Author_Institution :
Dept. of Metall. Eng., Seoul Nat. Univ., South Korea
fDate :
11/1/1995 12:00:00 AM
Abstract :
We have studied the effects of P addition in a new alloy system of Co-Cr-P-Pt with coercivity higher than 2600 Oe even when it was deposited without substrate heating and bias voltage. The addition of P increased the Co{1010} texture and decreased the Co{0002} texture, which is one of the reasons for the higher in-plane coercivity. The magnetization reversal mechanism changed from domain wall motion to curling type incoherent rotation with the addition of P. As the P content increases, δM gradually shifts from positive to negative. This can be associated with enhancement of grain isolation and the reduction of out-of-plane orientation with the addition of P
Keywords :
chromium alloys; cobalt alloys; coercive force; ferromagnetic materials; magnetic thin films; magnetisation reversal; phosphorus alloys; platinum alloys; Co-Cr-P-Pt; Co-Cr-P-Pt magnetic thin films; P addition; coercivity; curling type incoherent rotation; domain wall motion; grain isolation; magnetic interactions; magnetization reversal; microstructures; texture; Amorphous magnetic materials; Chromium; Coercive force; Glass; Heating; Magnetic films; Microstructure; Sputtering; Substrates; Voltage;
Journal_Title :
Magnetics, IEEE Transactions on