    Magnetic Properties of Sm2Fe17(C,N)x Melt-Spun Ribbons

  • Author

    Kurihara, K. ; Nakamura, H. ; Sugimoto, S. ; Okada, M. ; Homma, M.

  • Author_Institution
    Tohoku University.
  • Volume
    7
  • Issue
    12
  • fYear
    1992
  • Firstpage
    931
  • Lastpage
    936
  • Abstract
    The effects of nitrogenation on the magnetic properties of Sm2(Fe0.9M0.1)17C1.6 (M=Ga,Cr) melt-spun ribbons were studied. The melt-spun amorphous ribbons are crystallized at temperatures above 550°C, forming a phase with the TbCu7 type structure, and on heating to 680°C and above underwent a further transition to a phase with a Th2Zn17 type structure. Nitrogenation at 550°C for four hours enhances the magnetic properties of annealed ribbons. The Sm2(Fe0.9Cr0.1)17C1.6 ribbon annealed at 650°C, which consists of TbCu7 structure, exhibits a high post-nitrogenation (BH)max of 11.0 MGOe. Sm2(Fe0.9Cr0.1)17C1.6 ribbon annealed at 725°C, which consists of the Th2Zn17 structure, shows a high coercivity of 19.0 kOe with a (BH)max of 7.4 MGOe after nitrogenation.
  • Keywords
    Amorphous materials; Annealing; Chromium; Coercive force; Crystallization; Heating; Iron; Magnetic properties; Temperature; Zinc;
  • fLanguage
    English
  • Journal_Title
    Magnetics in Japan, IEEE Translation Journal on
  • Publisher
    ieee
  • ISSN
    0882-4959
  • Type

    jour

  • DOI
    10.1109/TJMJ.1992.4565539
  • Filename
    4565539
    • Link To Document
    https://search.isc.ac/dl/search/defaultta.aspx?DTC=49&DC=801626