Title :
Alignment of high-T/sub c/ superconductor Y/sub 1/Ba/sub 2/Cu/sub 3/O/sub z/ thick film in magnetic field
Author :
Young Cheol Kim ; Seok Kil Han ; Hyung Kook Kim ; Min Su Jang
Author_Institution :
Dept. of Phys., Pusan Nat. Univ., South Korea
fDate :
3/1/1993 12:00:00 AM
Abstract :
High-T/sub c/ superconducting thick films were prepared using a method combining grain shape alignment and low magnetic field alignment. The superconducting films with a thickness of about 100 mu m exhibiting T/sub c/(zero) higher than 90 K were successfully obtained. X-ray diffraction data showed the thick Y/sub 1/Ba/sub 2/Cu/sub 3/O/sub z/ film having grain alignment. The orientation along the c-axis is pronounced with an increase in the heat-treatment temperature and time in magnetic field.<>
Keywords :
X-ray diffraction examination of materials; barium compounds; heat treatment; high-temperature superconductors; materials preparation; powder technology; superconducting transition temperature; yttrium compounds; 100 micron; 800 C; X-ray diffraction; YBa/sub 2/Cu/sub 3/O/sub z/ thick film; grain shape alignment; heat-treatment temperature; high temperature superconducting thick film; low magnetic field alignment; magnetic field; resistivity; Magnetic fields; Magnetic films; Magnetic materials; Powders; Shape; Superconducting films; Superconducting magnets; Superconducting materials; Thick films; X-ray diffraction;
Journal_Title :
Applied Superconductivity, IEEE Transactions on